| Experimental record sheet | |||||
| Test name | Dispersant Comparison for Mitsubishi MA-100 Carbon Black | ||||
|
Objective: Comparative Testing: 6062, 6062A, 6062B, and Benchmark: 163 |
|||||
| Color paste formulation | |||||
| Sanmu 965 Hydroxy-functional Acrylic Resin | 60 | ||||
|
S01/S05/S07 Mixed Solvent (1:1:1 ratio) |
27 | ||||
| Dispersant | 3 | 6062 | 6062A | 6062B | Benchmark: 163 |
| MA-100 carbon black | 10 | ||||
| Procedure: | |||||
|
1.Grinding: Grind all ingredients together for 3 hours. 2.Quality Control: Measure the fineness (e.g., in μm). Observe and record the appearance and state (e.g., homogeneity, viscosity). 3.Color Development Test: Prepare draw-downs on black and white art paper to evaluate color development and strength. |
|||||
| Result | |||||
|
Best Performance: 6062A produced the blackest mass tone. Comparable Performance: 6062B and the standard 6062 showed essentially identical results. Benchmark Comparison: When evaluated against the benchmark: 163 |
|||||
| Fineness＜um | Fineness After Heat Aging | Flow State (Visual) | Appearance After Heat Aging | Color Draw-down Panel | |
| 6062 | 10 | 10 | Easy Flow | Easy flow with slight pseudo-plasticity | Qualified |
| 6062A | 10 | 10 | Easy Flow | Easily Flowable with Slight Charring | Excellent |
| 6062B | 10 | 10 | Easy Flow | Easy flow with slight pseudo-plasticity | Qualified |
| BYK163 | 10 | 10 | Easy Flow | Easy flow with slight pseudo-plasticity | Poor |
| |
|||||
| Conclusion | |||||
| Anjeka-6062A demonstrated the best color development, while 6062B and 6062 were slightly inferior. B163 showed the poorest performance. | |||||